The biology and physiology of Tyrophagus putrescentiae (Schrank) (Sarcoptiformes: Acaridae), also known as the ham, cheese or mold mite, is reviewed along with methods that have been evaluated for managing and controlling this pest. This review was conducted because the ham mite is an important target pest of the dry cured ham industry. Methyl bromide has been historically used to control mite infestations, but is now banned or being phased out of use in most countries because it is an ozone-depleting substance. Only commercially available stockpiles and quarantine and pre-shipment methyl bromide are available for use in countries that require such action. This review compares the effectiveness and feasibility of recently investigated methods to control mite infestations on dry cured ham and to discuss integrated pest management plans for ham mites. The review also proposes methods for conducting a prevention and monitoring-based integrated pest management program that relies on definitive mitigation such as fumigation only when mite numbers exceed a critical action threshold.     

含氢类金刚石涂层在船用柴油机柱塞上的应用

利用磁控溅射和等离子增强化学气相沉积复合技术,以 Cr、WC、石墨为靶材,Ar和C₂H₂为工作气体,在船用低速柴油机柱塞上涂覆了过渡层依次为Cr、WC的含氢类金刚石涂层。结果表明:涂层晶体生长良好,结构连续致密,均未出现分层、开裂及剥离的现象;涂层相对光滑,大幅度提高了柱塞表面的纳米硬度与弹性模量,同时降低了在重柴油环境下的摩擦因数,长时间的台架试验后未涂覆涂层的柱塞表面出现非常明显的平行状沟槽磨痕,而且整体磨损比较严重,而涂覆涂层的柱塞表面磨痕非常窄且浅,数量较少,类金刚石涂层可以明显提高柱塞表面的耐磨损性能。     

变形铝合金表面锆基化学转化膜的研究现状

化学转化膜是金属表面主要的处理方法之一，具备良好的附着力和耐蚀性，能为铝合金提供一定的临时防护。传统的六价铬酸盐化学转化膜在日渐严苛的环保压力下已经逐渐淘汰，取而代之的是近几年发展迅猛的三价铬及无铬锆基化学转化膜。铝合金可分为铸造铝合金和变形铝合金，按照所含主要合金元素和热处理状态可分为若干个系列和型号。本文选取几种典型的变形铝合金，综述了不同铝合金微观组织对转化膜成膜过程的影响，化学转化液添加剂、预处理和后处理工艺对转化膜性能的调控及作用机理，以及几种典型商业钝化剂在变形铝合金表面的应用。总结了目前变形铝合金表面锆基化学转化膜仍面临的问题和发展趋势，未来化学转化膜需在满足新型铝合金发展要求的基础上，通过不同有机、无机添加剂以及外场作用对转化膜的成膜均一性、完整性进行调控，以提高转化膜的综合性能。     

钼电极表面Y2O3-玻璃基涂层抗氧化性能研究

目的提高钼电极在玻璃炉窑烘窑过程中的抗氧化性能。方法在纯钼基体表面制备不同Y2O3含量的玻璃基抗氧化涂层。对涂层分别在800、1000、1200℃下进行抗氧化测试,利用扫描电镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)对涂层在氧化前后的形貌、成分和物相进行检测,利用热分析仪对涂层粉体进行差热分析(DTA)。结果随着Y2O3成分含量的增加,硅酸盐玻璃的软化点温度不断降低,晶化放热峰也越来越低。Y2O3含量为10%和20%的涂层表面结构完整,整体比较致密,在1200℃高温氧化条件下,在第1h内出现增重,之后随着加热时间的延长,增重趋于稳定。Y2O3含量为30%的涂层表面呈致密片状结构,部分出现脱落,样品在氧化过程中出现明显失重。结论Y2O3含量为10%的Y2O3-玻璃基涂层经过1200℃抗氧化实验后,表面完整,试样增重较少,性能优良。涂层截面分为过渡层、中间层和最外层。过渡层主要为MoO2和MoO3,中间层主要是BaMoO4,最外层主要是SiO2。涂层抗氧化机理为互熔反应型保护机理和惰性熔膜屏蔽型保护机理。     

纳米晶NiCrC涂层长时加热的显微组织和硬度变化

目的 探讨纳米晶NiCrC涂层长时高温条件下的显微组织和硬度演变规律。方法 采用超音速火焰（HVAF）喷涂低温球磨纳米晶合金粉末（液氮介质）制备了纳米晶NiCrC涂层，在650 ℃空气环境中对涂层进行总时长200 h的等温热处理。采用扫描电子显微镜、X射线衍射仪、透射电子显微镜、维氏显微硬度计等方法，对涂层样品的显微组织、物相构成、晶粒尺寸和显微硬度进行了测试分析，同时对原料粉末也进行了相同条件下的对比分析。结果 NiCrC涂层显微组织的主要特征为：纳米晶金属相基体中弥散分布着细小的碳化物颗粒。在保温过程中，纳米晶涂层发生了再结晶和晶粒长大，并伴随有合金基体的脱溶及碳化物的析出、相变和后续生长等现象。该涂层显示出优良的高温热稳定性，在650 ℃保温50 h后，晶粒平均尺寸由初始态的41 nm增长至相对稳定值约100 nm。保温后涂层的硬度总体有所提升，由初始的697HV300（15 s）先升高至最大值801HV300（15 s），而后降至相对稳定值729HV300（15 s）左右。纳米晶粉末的组织和硬度变化特点与涂层相似。结论 在650 ℃保温过程中，纳米晶NiCrC涂层中的合金相脱溶和晶粒长大导致涂层金属相基体的软化，但细小碳化物颗粒的析出强化以及由相变（Cr7C3→Cr23C6）引起的体积分数增加，不但补偿了基体的软化，而且使涂层的整体硬度有所提高。     

丝网印刷法制备Y改性CuMn2O4尖晶石涂层研究

目的 提高SOFC金属连接件CuMn2O4尖晶石涂层高温抗氧化性能和导电性能。方法 采用溶胶-凝胶法制备Y改性CuMn2O4尖晶石粉末，采用丝网印刷技术在SUS430合金表面制备Y改性CuMn2O4尖晶石涂层。利用XRD、SEM表征Y改性CuMn2O4尖晶石粉体及涂层的物相结构及微观形貌。利用氧化增重实验研究Y改性前后CuMn2O4尖晶石涂层试样在800 ℃空气中氧化168 h的高温氧化行为，通过“四点法”测量涂层在高温氧化过程中的面比电阻值。结果 CuMn2O4尖晶石粉末的晶格常数随着稀土Y含量的增大而增大，当Y元素的含量为0.02 mol/L时，晶格常数增幅趋于平缓，此时所得粉体物相结构稳定，结晶程度较好，晶粒尺寸细小且颗粒间团聚现象较少。Y改性前后CuMn2O4尖晶石涂层试样的氧化动力学曲线均遵循抛物线氧化定律，其氧化速率常数分别为9.39×10-5、6.31×10-5 mg2/(cm4?h)。Y改性CuMn2O4尖晶石涂层试样在800 ℃氧化168 h时的面比电阻值约为26.2 m??cm2，低于未改性涂层试样的面比电阻值（约27.3 m??cm2）。结论 Y改性CuMn2O4尖晶石涂层能有效改善金属连接体的高温抗氧化性能和导电性能。     

低压冷喷涂Cu-Zn复合涂层耐蚀性能的研究

本文使用低压冷喷涂技术，分别在45#钢基体与45#钢加镀铬层基体上制备铜锌涂层试样。通过静态浸泡与铜加速醋酸盐雾腐蚀试验（CASS）对涂层和涂层加镀铬层试样的腐蚀性能进行研究；采用SEM、XPS对腐蚀前后涂层与镀铬层的微观形貌与元素进行表征。结果表明：静态腐蚀过程中，铜锌涂层的耐腐蚀性优于铜锌涂层加镀铬层；CASS实验中，随着原始粉体中锌含量的增加，涂层试样与涂层加镀铬层试样的耐腐蚀性能提高，当铜锌比为6:4时，对应涂层试样、涂层加镀铬层试样与纯镀铬层的耐腐性能达到六级。铜锌涂层在腐蚀液中由于电化学腐蚀及氯化作用，导致铜锌均发生了腐蚀，其腐蚀产物主要为Zn(OH)2、Cu2O与CuCl2。铜锌涂层加镀铬层试样在腐蚀过程中，锌的腐蚀在一定成上可以起到减缓镀铬层腐蚀的作用，这种减缓的作用与镀铬层上析出的铜膜共同保护镀铬层，增强其耐腐蚀性能。     

金属有机框架衍生的Bi/C复合材料作为钠离子电池负极材料的研究

金属铋(Bi)用作钠离子电池的负极材料具有较高的理论比容量和较低的嵌钠电位,但是在钠离子嵌入和脱出的过程中容易发生较为严重的体积膨胀,从而导致循环性能较差。为改善金属Bi负极的循环性能,将其与具有多孔结构的碳复合是一种有效的改善手段。在过去几年中,金属有机框架(metal-organic frameworks,MOFs)作为一种合成前驱体被广泛应用于各种金属氧化物及多孔碳材料的合成中。合成了一种含铋的金属有机框架材料,并以其为前驱体,再经高温煅烧合成了多孔碳包覆的金属铋复合材料,该复合材料中的碳骨架及其丰富的孔结构能有效缓解Bi在钠离子脱嵌过程中的体积膨胀,从而提高其循环稳定性。     

时效处理对高频感应熔覆TiC/Ni复合涂层的组织及性能影响

为了改善抽油杆材料的表面性能,采用高频感应熔覆技术在其表面制备了TiC/Ni复合涂层。采用光学显微镜、扫描电镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)等研究了涂层经固溶及不同时间时效处理后的显微组织及物相组成,并利用显微硬度计及摩擦磨损实验测试了时效后涂层的性能变化。结果表明:经固溶时效后的涂层并未出现明显缺陷,涂层主要以γ-Ni固溶体、Ni的化合物、CrB、碳化物以及δ相等硬质颗粒组成;时效后涂层的最大硬度达到928.2 HV0.2,相比时效前提高了4%,最低磨损量为48.9 mg,比基材减少了62%,在时效4 h后,涂层的综合性能最好。     

Mechanical properties,oxygen barrier property,and chemical stability of RE3NbO7 for thermal barrier coating

Rare earth niobate (RE₃NbO₇, RE = Dy, Y, Er, Yb) ceramics have shown extremely low thermal conductivity but remain questionable in high temperature thermal barrier coating (TBC) applications with high thermal, mechanical, and chemical loads. Herein, we comprehensively characterize the properties of rare earth niobates, including mechanical properties, oxygen barrier properties, chemical stability, etc. It is found that the oxygen conductivities of the rare earth niobates are three orders of magnitude lower than 7wt.% yttria-stabilized zirconia (YSZ), indicating a remarkable oxygen barrier property to avoid oxidation of underlying metallic components. The corrosion resistance of rare earth niobate against calcium-magnesium-aluminum silicate (CMAS) is also significantly better than that of YSZ. Together with the extremely low thermal conductivity, the rare earth niobates exhibit a combination of excellent high temperature properties, which may become a promising candidate material of high temperature TBC of next generation gas turbines.